Method of Recovering Valuable Metal from Scrap Containing Conductive Oxide

ABSTRACT

Proposed is a method of recovering valuable metal from scrap containing conductive oxide including the steps of using an insoluble electrode as either an anode or a cathode, using a scrap containing conductive oxide as the counter cathode or anode, performing electrolysis while periodically inverting the polarity, and recovering the scrap as hydroxide. With the foregoing method of recovering valuable metal from scrap containing conductive oxide, oxide system scrap is conductive oxide and a substance that can be reduced to metal or suboxide with hydrogen. This method enables the efficient recovery of valuable metal from sputtering target scrap containing conductive oxide or scrap such as mill ends of conductive oxide that arise during the production of such a sputtering target.

TECHNICAL FIELD

The present invention relates to a method of recovering valuable metal from scrap containing conductive oxide as represented by an ITO scrap of a spent indium-tin oxide (ITO) sputtering target or an ITO scrap such as ITO mill ends (hereinafter collectively referred to as “scrap containing conductive oxide” in this specification). Incidentally, the phrase “recovery of valuable metal” as used herein shall include compounds of oxides and hydroxides having valuable metal as its component.

BACKGROUND ART

In recent years, an indium-tin oxide (In₂O₃—SnO₂: generally known as ITO) sputtering target is being widely used in numerous electronic components; for instance, for a transparent conductive thin film of an LCD device or a gas sensor. In many cases, however, it is used as a result of a thin film being formed on a substrate or the like by employing the sputtering method as the thin film forming means. ITO is a representative oxide with conductive property.

Oxide with conductive property (conductive oxide) is not limited to ITO, and there are numerous conductive oxides including IGZO (In—Ga—Zn—O composite oxide), ZnO, Zn—SnO₂, SnO₂, Co—In—O composite oxide, Ni—Sn—O composite oxide, Cu—Ga—O composite oxide, Pb—Sn—O composite oxide, Cd—Zn—O composite oxide, Ca-Gu-O composite oxide, Sb—In—O composite oxide, Fe—Ge—O composite oxide, Pb—Sn—O composite oxide, Ti—In—O composite oxide, and the like. These composite oxides are similarly used for preparing a target, sputtering the target to form a thin film, and thereby used in various electronic components.

It is true that the sputtering method as the thin film forming means is superior, but when a sputtering target is used to form a transparent conductive thin film of the like, the target will not be consumed uniformly. A portion of the target with severe consumption is generally referred to as an eroded portion, and the sputtering operation is continued until immediately before a backing plate supporting the target becomes exposed due to the further consumption of the eroded portion. This target is subsequently replaced with a new target.

Accordingly, a spent sputtering target will have numerous non-eroded portions, that is, unused portions of the target, and all of these portions become scrap. Moreover, even in the production of a sputtering target formed from such conductive oxides, scraps (mill ends) will arise from abrasive powder, cutting powder and the like.

High purity materials are used as the sputtering target material formed from the foregoing conductive oxides and, since all of these materials are expensive, the process of recovering raw materials from scrap materials is being generally performed. As this kind of high purity material recovery method, conventionally, a method that combines wet refining such as the acid solution process, ion exchange method, and solvent extraction method has been used.

For instance, there is a method of subjecting an ITO scrap to cleansing and pulverization, thereafter dissolving this in hydrochloric acid, precipitating and eliminating impurities such as zinc, tin, lead and copper as sulfide by passing hydrogen sulfide through the solution, thereafter adding ammonia to neutralize the solution, and recovering the resulting indium hydroxide.

Nevertheless, the indium hydroxide obtained with the foregoing method has inferior filtration property, requires long operational process, and contains large amounts of impurities such as Si and Al. In addition, with the created indium hydroxide, since the grain size and grain size distribution will vary depending on the neutralization condition, maturization condition and other conditions, there is a problem in that the characteristics of the ITO target cannot be stably maintained upon subsequently manufacturing such ITO target. The same applies to other conductive oxides.

Conventional technology and its advantages and disadvantages are described below.

As one example of such conventional technology, there is an etching method of a transparent conductive film including the steps of reducing an ITO film deposited on a substrate based on an electrochemical reaction in the electrolyte, and dissolving the reduced transparent conductive film in the electrolyte (refer to Patent Document 1). However, the object of this method is to obtain a mask pattern with high precision, and relates to technology that is different from the recovery method.

There is also technology of separating, in the electrolyte, the impurities contained in an In brazing filler material used in the bonding with the backing plate as pretreatment for recovering valuable metal from ITO (refer to Patent Document 2). Nevertheless, this method does not relate to technology of directly recovering valuable metal from ITO.

Moreover, upon recovering indium from an intermediate obtained as a by-product of the zinc refining process or an ITO scrap, disclosed is technology of separating tin as halogenated stannate, performing reduction treatment with hydrochloric acid or a nitric acid solution, subsequently adjusting the pH of this aqueous solution to 2 to 5, reducing metallic ions of iron, zinc, copper, thallium and the like in order to obtain a substance that will not precipitate easily, and separating the indium component in the aqueous solution (refer to Patent Document 3). With this technology, however, there is a problem in that the refining process is complicated, and a superior refining effect cannot be expected.

Further, as a method of recovering high purity indium, disclosed is technology of dissolving ITO in hydrochloric acid, adding alkali thereto to make the pH 0.5 to 4, eliminating tin as hydroxide, subsequently blowing hydrogen sulfide gas in order to eliminate hazardous materials such as copper and lead as sulfide, and electrowinning indium metal by performing electrolysis using the obtained solution (refer to Patent Document 4). There is a problem with this technology in that the refining process is complicated.

In addition, proposed is a method of dissolving an ITO indium-containing scrap in hydrochloric acid to obtain an indium chloride solution, adding a sodium hydroxide solution to this solution to eliminate tin as tin hydroxide, additionally adding a sodium hydroxide solution after the elimination to obtain indium hydroxide, filtering the obtained indium hydroxide, obtaining indium sulfate from the filtered indium hydroxide, and obtaining indium by electrowinning the indium sulfate (refer to Patent Document 5). Although this is an effective method with a significant refining effect, there is a drawback in that the process is complicated.

Also proposed is a method of recovering indium including the steps of dissolving an ITO indium-containing scrap in hydrochloric acid to obtain an indium chloride solution, adding a sodium hydroxide solution to the indium chloride solution to eliminate tin contained in the scrap as tin hydroxide, substituting indium with zinc from the solution after eliminating the tin hydroxide, and thereafter recovering indium (refer to Patent Document 6). Although this is also an effective method with a significant refining effect, there is a drawback in that the process is complicated.

Additionally disclosed is a method of recovering metallic indium including the steps of extracting suboxide-containing cast scrap floating on molten metal indium and introducing this into an atmosphere furnace, vacuating the furnace once, thereafter introducing argon gas, heating the furnace to a prescribed temperature and reducing the suboxide-containing cast scrap (refer to Patent Document 7).

Although this is in itself an effective method, there is a drawback in that this is not a fundamental recovery method of conductive oxide.

In light of the above, a method that is efficient and has a versatile recovery process is being sought.

[Patent Document 1] Japanese Patent Laid-Open Publication No. S62-290900 [Patent Document 2] Japanese Patent Laid-Open Publication No. H8-41560 [Patent Document 3] Japanese Patent Laid-Open Publication No. H3-82720

[Patent Document 4] Japanese Patent Laid-Open Publication No. 2000-169991 [Patent Document 5] Japanese Patent Laid-Open Publication No. 2002-69684 [Patent Document 6] Japanese Patent Laid-Open Publication No. 2002-69544 [Patent Document 7] Japanese Patent Laid-Open Publication No. 2002-241865 DISCLOSURE OF THE INVENTION

In order to overcome the foregoing problems, the present invention provides a method of efficiently recovering valuable metal from sputtering target scrap containing conductive oxide or a scrap such as mill ends arose during the manufacture of such sputtering target.

The present invention provides a method of recovering valuable metal from scrap containing conductive oxide by subjecting the scrap containing conductive oxide to electrolysis in pH-adjusted electrolyte, and thereby recovering valuable metal as hydroxide. Here, the present invention can be applied to all oxides as long as it is a conductive oxide and, regardless of the level of conductive property, contains an element that can be reduced to metal or suboxide with hydrogen.

The method of recovering valuable metal from scrap containing conductive oxide according to the present invention has a significant feature of using an insoluble electrode as the anode or cathode, and using scrap containing conductive oxide as the counter cathode or anode. In this case, electrolysis is performed by periodically inverting the polarity of both the anode and cathode; that is, electrolysis is performed by alternately changing the polarity periodically (mutual inversion of anode polarity

cathode polarity).

It is thereby possible to efficiently recover the scrap as hydroxide. No such technology existed conventionally, nor is there any document that suggests this kind of method. Thus, the method of recovering valuable metal from scrap containing conductive oxide according to the present invention is a basic invention.

Since scrap containing conductive oxide is an oxide system ceramic, it would not be possible to envisage recovering valuable metal with the electrolytic method under normal conditions. Nevertheless, the substance itself to be recovered in the present invention possesses conductive property even though it is an oxide system ceramic. The present invention focused attention on this point and attempted to recover valuable metal with electrolysis, and succeeded.

It is well known that the foregoing substances including ITO possess conductive property. Taking ITO as an example, this is considered to be a result of the oxygen defect of ITO as the sintered compact of tin oxide (SnO₂) and indium oxide (In₂O₃). The same applies to the other conductive oxides described above.

The present invention utilizes the conductive property of the substance itself. Nevertheless, it should be understood that the knowledge and judgment that the recovery of valuable metal based on electrolysis utilizing the conductive property inherent to substances such as ITO could only be realized through the implementation of numerous experiments.

For example, with a conventional method of recovering valuable metal from scrap containing conductive oxide such as ITO, a plurality of processing steps are combined such as pulverizing the scrap and dissolving it in strong acid, and then subjecting it to reduction, substitution, sulfurization, precipitation, neutralization, filtration, solvent extraction, ion exchange, casting and so on.

The problem during the foregoing processing steps is the inclusion of impurities during the pulverization process of the scrap containing conductive oxide, and, since it will be necessary to eliminate the impurities mixed in during the pulverization process at the subsequent processing steps, the overall process will become more complicated.

Thus, it should be easy to understand that directly recovering valuable metal from scrap containing conductive oxide based on electrolysis yields a highly significant advantage.

With the method of recovering valuable metal from scrap containing conductive oxide according to the present invention, it is desirable to invert the polarity of the anode and cathode at the time the voltage during the electrolysis rises to a certain level or higher. As described later, the conversion of polarity of the anode and cathode is a means for improving the recovery efficiency, and the voltage is used as the index thereof. Thus, the timing of inverting the polarity can be set according to the detection of the rise in voltage.

Generally, once the equipment is fixed, the constant optimal condition for the timing of inversion can be understood and the polarity may also be inverted at certain timing. Accordingly, the timing of inverting the polarity of the anode and cathode polarity can be controlled arbitrarily, and it should be easily understood that such timing of inversion is not bound by the foregoing conditions.

Moreover, during the foregoing electrolysis, it is preferable to invert the polarity of the anode and cathode in 1 minute to 10 minute cycles. However, the timing of inverting the polarity is also a condition that may be arbitrarily changed according to the capacity of the electrolytic bath, amount of scrap containing conductive oxide, current density, voltage, current, type of electrolyte and so on. The foregoing conditions merely show the preferable conditions, and it should be easily understood that the timing of inversion is not bound by the foregoing conditions either.

Upon recovering valuable metal from scrap containing conductive oxide according to the present invention, after performing electrolysis, the scrap can be recovered as hydroxide. For example, in the case of an ITO scrap as the representative scrap, it is desirable to adjust the pH of the initial electrolyte to be 2 to 12. This is a preferable condition for efficiently recovering the scrap as hydroxide.

Here, if the pH is less than pH 2 or exceeds pH 12, the scrap containing conductive oxide will dissolve as ions and become electrodeposited, and the efficiency will thereby deteriorate. Nevertheless, even if the pH is less than pH 2 or exceeds pH 12, the foregoing inconvenience can be overcome by precipitating the scrap containing conductive oxide as metastannic acid by adding nitric acid ions and the like. Thus, it is not necessary to limit the pH to be between 2 to 12. Moreover, another reason that it is not necessary to limit the value to the foregoing range is because other substances (scraps) have different ranges in which hydroxide is created depending on the type of such substance (scrap). The present invention covers all of the foregoing aspects.

As described above, the pH may be selected arbitrarily. The essence of the present invention is to recover valuable metal from scrap containing conductive oxide as hydroxide by performing electrolysis while periodically inverting the polarity. As long as there is no known technology related to the foregoing method, there is no reason to limit the pH to the foregoing range. Moreover, even if the pH is subsequently devised or improved, it is evident that such devisal or improvement is within the technical scope of, and covered by, the present invention.

As the electrolyte, it is desirable to select a solution that does not emit hazardous gases, and a material that will not be contained as an impurity in the substance upon recovering the scrap as hydroxide. In light of the above, a solution of sodium sulfate, sodium chloride, sodium nitrate, ammonium sulfate, ammonium chloride, ammonium nitrate, potassium chloride, potassium nitrate, potassium sulfate and the like may be arbitrarily selected and used.

Nevertheless, as long as it is a solution that gives consideration to the production efficiency and can be used for subjecting the scrap containing conductive oxide to electrolysis, it should be understood that solutions other than those indicated above may also be used as the electrolyte. The selection of a solution as the electrolyte can be made arbitrarily as long as the solution satisfies the conditions for subjecting the scrap containing conductive oxide to electrolysis, and it is evident that such selection is not the essence of the present invention.

In the recovery of valuable metal from scrap containing conductive oxide, the present invention has achieved its object by recovering the hydroxide obtained from the electrolysis. However, it is also possible to roast the hydroxide to recover metal oxide or a mixture of two or more types of metal oxides.

As described above, if hydroxide can be once recovered from scrap containing conductive oxide, it will be possible to roast this to obtain metal oxide or a mixture of two or more types of metal oxides, and use this as is as the raw material of the target conductive oxide material. Further, as needed, other oxides or metals may be added to change the component amount, and it would be easy to sinter this and once recycle it as a new conductive oxide target. The present invention covers all of the foregoing aspects.

In addition, it is also possible to subject the hydroxide obtained from the foregoing electrolysis to acid leaching in order to obtain a solution containing metal, and adjust the pH of this solution to extract the respective target metals.

As described above, the recovery of valuable metal from scrap containing conductive oxide according to the present invention enables to maintain the purity without change if the scrap containing conductive oxide to be subject to electrolysis is in itself scrap of a high purity material, and the scrap can be recovered as high purity hydroxide or metal oxide or a mixture of two or more types of metal oxides.

It is obvious that this is a significant advantage of the present invention. The present invention yields superior effects of saving complicated processes and the process of eliminating impurities mixed in during production as in the past, enabling to increase the production efficiency, and recover high purity valuable metal.

The electrolytic condition such as the current density and the like is not uniformly decided since the subject is scrap such as mill ends, and the current density is suitably selected and implemented according to the amount of mill ends and the quality of material. The liquid temperature of the electrolyte solution is generally set to a range of 0 to 100° C., but room temperature (15 to 30° C.) will suffice.

The method provided by the present invention is superior, since recovering valuable metal from scrap containing conductive oxide, such scraps as a sputtering target scrap containing conductive oxide or a scrap as mill ends of conductive oxide that arise during the production of such a sputtering target, is simply subject to electrolysis as an insoluble electrode and cathode formed from scrap. It is very easy to obtain hydroxide and efficiently recover the same. Moreover, the recovery of valuable metal from scrap containing conductive oxide according to the present invention enables to maintain the purity without change if the scrap containing conductive oxide to be subject to electrolysis is in itself scrap of a high purity material, and the scrap can be recovered as high purity hydroxide or a mixture of various oxides. This is a significant advantage of the present invention. The present invention yields superior effects of saving complicated processes and the process of eliminating impurities mixed in during production as in the past, enabling to improve the production efficiency and recover high purity valuable metal.

BEST MODE FOR CARRYING OUT THE INVENTION

The present invention enables to easily recover scrap such as mill ends containing conductive oxide as hydroxide based on electrolysis. By additionally roasting the obtained hydroxide, the scrap can be efficiently recovered as various metal oxides or a mixture thereof.

The roasting temperature is set to 100 to 1000° C., preferably 100 to 500° C. Moisture will remain if the roasting temperature is less than 100° C. and sintering will occur if the roasting temperature is higher than 1000° C. Thus, the roasting temperature is set to be within the foregoing range.

Nevertheless, the roasting temperature may be selected arbitrarily. The essence of the present invention is to recover valuable metal from scrap containing conductive oxide as hydroxide by performing electrolysis while periodically inverting the polarity. As long as there is no known technology related to the foregoing method, there is no reason to limit the roasting temperature to the foregoing range. Moreover, even if the roasting temperature is subsequently devised or improved, it is evident that such devisal or improvement is within the technical scope of, and covered by, the present invention.

As the electrolyte, a solution such as sodium sulfate, sodium chloride, sodium nitrate, ammonium sulfate, ammonium chloride, ammonium nitrate, potassium chloride, potassium nitrate, potassium sulfate may be arbitrarily selected and used.

Further, caution is necessary in the processing since chlorine gas will be generated pursuant to the passivation of the anode if the anion is a chlorine anion, and since nitric oxide gas will be generated pursuant to the passivation of the anode if the anion is a nitric acid anion and there will a nitrogen load of the discharged water.

Since a sulfuric acid system hardly entails the foregoing problems, it could be said that a sulfuric acid solution would be a suitable material. Nevertheless, there is no reason that other electrolytes cannot be used as long as the foregoing problems can be overcome.

In addition, it is also possible to use a publicly-known additive agent in order to improve the current efficiency.

A special electrolytic apparatus is not required. For instance, the method of recovering valuable metal from scrap containing conductive oxide according to the present invention has a significant feature of using an insoluble electrode as the anode or cathode, and using scrap containing conductive oxide as the counter cathode or anode. Whether an insoluble electrode or scrap containing conductive oxide is to be used as the initial anode or cathode is not important, because the polarity is periodically inverted. It should be easily understood that the present invention is applicable to both cases.

It is thereby possible to avoid the increase or inclusion of impurities initially contained in the scrap containing conductive oxide. A publicly-known insoluble electrode may be used as the foregoing insoluble electrode. Although carbon or the like is a preferable material, there is no need to limit the insoluble electrode to carbon or the like. Electrodes that are generally referred to as an “insoluble electrode” can all be used. It should be easy to understand that the selection of the insoluble electrode is not the essence of the present invention.

It is desirable to adjust the electrolytic condition as needed according to the type of raw material. The only factor to be adjusted in this case is the production efficiency. Generally, better productivity can be attained through electrolysis with a large current and high voltage. Nevertheless, there is no need to limit the conditions to the foregoing conditions, and such conditions may be arbitrarily selected.

Further, although there is no particular limitation on the electrolysis temperature, it is desirable to perform electrolysis upon adjusting the temperature to 0 to 100° C. Electrolysis can be sufficiently performed at room temperature. Scraps such as mill ends may be placed in a cathode box (basket) for the electrolysis. If a scrap itself is of a prescribed size (size that can be used as an electrode), it can be used as an electrode plate as is.

When the insoluble electrode or the cathode formed from scrap containing conductive oxide is energized and electrolysis is commenced, oxygen gas will be generated in the insoluble anode. However, the generation of oxygen gas will not cause any particular problem.

Hydrogen gas is generated together with the commencement of energization in the cathode of the scrap containing conductive oxide, and the scrap containing conductive oxide is subject to hydrogen reduction and becomes metal. For example, if the scrap is ITO, it will become indium-tin metal (ITO+H₂→In—Sn metal). The generation of hydrogen is caused by the electrolysis of water (H₂O→½H₂+OH⁻).

The metal is accumulated on the surface of the cathode of such scrap containing conductive oxide, and partially precipitates as hydroxide.

Nevertheless, if the energization time takes long, slightly thick metal is formed on the surface of the cathode of the scrap containing conductive oxide, and sponge-shaped metal suboxide will merely be formed below the metal surface layer, and the reduction will not progress any further.

The primary reason for the obstruction in progress of electrolysis is considered to be because the metal surface layer is inhibiting the infiltration of hydrogen, current only flows to the metal surface layer and the flow of current inside the scrap containing conductive oxide is inhibited. Under the circumstances, the targeted electrolysis will be inhibited in the cathode of the scrap containing conductive oxide. Here, the polarity of the anode and the polarity of the cathode of the scrap containing conductive oxide are inverted. This is particularly an important process.

The metal that was accumulated on the surface of the new anode (ex cathode) will dissolve. Since the electrolyte is retained in a neutral region, it will precipitate as hydroxide. The precipitate obtained thereby can be recovered as hydroxide. For instance, taking ITO as an example, the primary reaction formula will be (In—Sn→In³⁺+Sn²⁺→In(OH)₃+Sn(OH)₂). Slight generation of oxygen is acknowledged in the new anode.

Meanwhile, since an insoluble electrode is used as the new cathode (ex anode), there is no substantial change, and there is only some generation of hydrogen gas.

Through the foregoing process, precipitation of the hydroxide mixture is promoted. Nevertheless, if this status is continued, only the surface layer of the new cathode will once again be subject to metalation, energization will not occur internally, and the electrolysis will stop progressing. The polarity is converted once again before falling into this kind of state. By repeating this process, precipitation of hydroxide can constantly be promoted.

By adopting this process of periodically inverting the electrodes, the gas generated in the electrode, that is, the generation of hydrogen and oxygen decreases significantly in comparison to cases of using either the anode or cathode as a fixed electrode. This implies that the generated gas is being effectively consumed for oxidation and reduction.

The conversion of polarity of the anode and cathode is a means for improving the recovery efficiency, and the voltage is used as the index thereof. Thus, the timing of inverting the polarity can be set according to the detection of the rise in voltage. Once the equipment is fixed, the constant optimal condition for the timing of inversion can be understood, and the polarity may also be inverted at certain timing.

Moreover, according to the experiments conducted, it is preferable to invert the polarity of the anode and cathode in 1 minute to 10 minute cycles. However, the timing of inverting the polarity is also a condition that may be arbitrarily changed according to the capacity of the electrolytic bath, amount of scrap containing conductive oxide, current density, voltage, current, type of electrolyte and so on.

EXAMPLES

The present invention is now explained in detail with reference to the Examples. These Examples are merely illustrative, and the present invention shall in no way be limited thereby. In other words, various modifications and other embodiments based on the technical spirit claimed in the claims shall be included in the present invention as a matter of course.

Example 1

The amount of 90 g plate-shaped mill ends (scrap) of ITO (indium oxide-tin oxide) having 20 mm (width)×100 mm (length)×6 mm (thickness) was used as the raw material. The components in this raw material were 9.8 wt % of tin oxide (SnO₂), and the remainder indium oxide (In₂O₃).

The raw material was used as the cathode, and carbon as an insoluble anode was used as the anode. Electrolysis was performed using 1 L of electrolyte containing 70 g/L of sodium sulfate, pH of 4.0, and electrolysis temperature of 30° C.

The voltage was 10V (fixed voltage), the current was 2.95 A (start) to 1.2 A (end), and the energization time (polarity conversion at a cycle of 5 minutes×12) was a total of 60 minutes (1 hour).

Consequently, the ITO mill ends showed a reduction of approximately 2.1 g. A mixture of indium hydroxide and tin hydroxide precipitated in the electrolytic bath.

It was thereby possible to obtain approximately 2.2 g (In quality level of 69.23 wt %) of In(OH)₃ and approximately 0.2 g (Sn quality level of 7.73 wt %) of Sn(OH)₂. Purity of the mixture of indium hydroxide and tin hydroxide or metastannic was the same as the purity of the scrap.

Example 2

The mixture of indium hydroxide and tin hydroxide or metastannic acid obtained as described above was further roasted at 150° C. in order to obtain a mixture of In oxide (In₂O₃) and Sn oxide (SnO₂). This mixture was roughly 2.0 g. The ratio obtained with this method was generally 90 wt % of In₂O₃ and 10 wt % of SnO₂, and was usable as the raw material of recycled ITO.

Example 3

The mixture of indium hydroxide and tin hydroxide or metastannic acid obtained with electrolysis was further subject to acid leaching with sulfuric acid to obtain a solution of indium and tin, this solution was adjusted to pH 2.0 to eliminate tin as tin hydroxide, and indium was further subject to electrowinning under the conditions of electrolysis temperature of 30° C. and current density of 2 A/dm².

As a result of the foregoing process, it was possible to recover approximately 1.5 g of valuable metal (In) from an ITO scrap.

Example 4

ITO mill ends of Example 1 were used as the cathode, Pt was used as the anode, 100 g/L of sodium nitrate solution was used as the electrolyte, pH was set to 10, and electrolysis was performed. Consequently, indium hydroxide and metastannic acid were obtained. The recovered amount and purity in this case were equivalent to Example 1.

Example 5

The amount of current was fixed at 2 A, and the setting was configured such that the polarity is inverted when the voltage reaches 10V or higher. The other conditions including the amount of accumulated current were the same as Example 1.

The recovered amount and purity were roughly equivalent to Example 1.

Example 6

The cycle was changed to 1 minute, and, with the other conditions being the same as Example 1, electrolysis was performed. Consequently, the recovered amount and purity were equivalent to Example 1.

Example 7

The cycle was changed to 10 minutes, and, with the other conditions being the same as Example 1, electrolysis was performed. Consequently, a mixture of approximately 1.7 g of In oxide (In₂O₃) and Sn oxide (SnO₂) was obtained. The purity of the mixture was equivalent to Example 1.

Example 8

The amount of 10 kg of ITO mill ends was placed in a cathode box, Pt was used as the anode, and electrolysis was performed with 100 g/L of sodium chloride as the electrolyte, and pH of 10.5. Polarity conversion was conducted in 5 minute intervals, and amount of accumulated current of electrolysis was 10000 AHr. Consequently, a mixture of approximately 6 kg of In oxide (In₂O₃) and Sn oxide (SnO₂) was obtained. Purity of the obtained mixture was roughly equivalent to Example 1.

Comparative Example 1

ITO scraps equivalent to Example 1 were used as the cathode, and insoluble carbon was used as the anode. The electrolytic conditions were the same as Example 1. Consequently, although indium-tin metal was obtained in the cathode, it was only on the cathode surface, and the overall cathode was not subject to metalation. Thus, it was not possible to efficiently recover valuable metal.

In each of the foregoing Examples, ITO (indium oxide-tin oxide) mill ends or scraps in which the components thereof were 9.7 wt % of tin oxide (SnO₂) and the remainder indium oxide (In₂O₃) were used, but it is obvious that the electrolytic conditions such as the current density and pH can be arbitrarily changed according to the component amount of In₂O₃ and SnO₂. There is no reason to be particularly limited by the component amount of the raw material. In particular, with ITO, the content of tin oxide (SnO₂) can be changed from 5 wt % to 30 wt %, and the present invention can also be sufficiently applied in the foregoing cases.

In addition, although there are cases where small amounts of accessory components are added to the ITO, as long as ITO is the basic constituent, it is obvious that the present invention is also applicable to this case.

Thus, the present invention efficiently enables the recovery of valuable metal from ITO scraps as a mixture of indium hydroxide and tin hydroxide or metastannic acid by using an insoluble electrode as either the anode or cathode, and using an ITO scrap as the counter cathode or anode, and changing the polarity. Examples other than ITO are now explained.

Example 9 Scrap to be Recovered: IGZO (In—Ga—Zn—O Composite Oxide)

Carbon as the insoluble anode was used as the anode. Using IGZO plate-shaped mill end scraps as the counter electrode, electrolysis was performed using 1 L of electrolyte containing 70 g/L of sodium sulfate, pH of 9, and temperature of 20° C. Electrolysis was performed by converting the polarity periodically (cathode→anode→cathode . . . ) when the voltage reached 10V. Consequently, hydroxides of In, Ga, and Zn were obtained. The production yield was 91%.

Then, a normally employed wet method (acid leaching→solvent extraction→electrolysis, etc.) was used to recover metals or oxides of In, Ga, and Zn.

As described above, with IGZO (In—Ga—Zn—O composite oxide) having conductive property, it was possible to efficiently recover valuable resources (metal).

Example 10 Scrap to be Recovered: ZnO

Carbon as the insoluble anode was used as the anode. Using ZnO plate-shaped mill end scraps as the counter electrode, electrolysis was performed using electrolyte containing 50 g/L of ammonium sulfate, pH of 10, and temperature of 50° C. Electrolysis was performed by periodically converting the polarity when the voltage reached 15V. Consequently, hydroxide of Zn was obtained. The production yield was 99.5%. The purity was the same as the starting material (purity of the raw material).

As a result of subjecting this hydroxide once again to desiccation and sintering, it was usable as a ZnO target. As described above, it was possible to efficiently recover ZnO as an oxide with conductive property.

Example 11 Scrap to be Recovered: ZnO—SnO₂

Carbon as the insoluble anode was used as the anode. Using ZnO—SnO₂ mill end scraps as the counter electrode, electrolysis was performed using electrolyte containing 100 g/L of sodium sulfate, pH of 9, and electrolysis temperature of 70° C.

During the electrolysis, the polarity was periodically inverted every 5 minutes. Consequently, hydroxides of Zn and Sn were obtained. The production yield was 99.0%. As described above, it was possible to efficiently recover ZnO—SnO₂ (conductive oxide) as the hydroxides of Zn and Sn.

Example 12 Scrap to be Recovered: SnO₂

Carbon as the insoluble anode was used as the anode. SnO₂ mill end scraps were used as the counter electrode and subject to electrolysis in a 70 g/L of sodium sulfate solution, pH of 2, and electrolysis temperature of 30° C. Electrolysis was performed by periodically inverting the polarity every 10 minutes. Consequently, hydroxide of Sn was obtained. The production yield was 99.7%. As described above, it was possible to efficiently recover SnO₂ (conductive oxide) as the hydroxide of Sn.

Example 13 Scrap to be Recovered: Co—In—O Composite Oxide

As with Example 9, electrolysis was performed with pH 9 while periodically inverting the polarity to obtain hydroxide. The production yield was 97.0%.

As with Example 9, with the Co—In—O composite oxide having conductive property, it was possible to efficiently recover a valuable resource (metal) as hydroxide.

Example 14 Scrap to be Recovered: Ni—Sn—O Composite Oxide

As with Example 9, electrolysis was performed with pH 7 while periodically inverting the polarity to obtain hydroxide. The production yield was 98.2%.

As with Example 9, with the Ni—Sn—O composite oxide having conductive property, it was possible to efficiently recover a valuable resource (metal) as hydroxide.

Example 15 Scrap to be Recovered: Cu—Ga—O Composite Oxide

As with Example 9, electrolysis was performed with pH 9 while periodically inverting the polarity to obtain hydroxide. The production yield was 99.1%.

As with Example 9, with the Cu—Ga—O composite oxide having conductive property, it was possible to efficiently recover a valuable resource (metal) as hydroxide.

Example 16 Scrap to be Recovered: Pb—Sn—O Composite Oxide

As with Example 9, electrolysis was performed with pH 10 while periodically inverting the polarity to obtain hydroxide. The production yield was 99.5%.

As with Example 9, with the Pb—Sn—O composite oxide having conductive property, it was possible to efficiently recover a valuable resource (metal) as hydroxide.

Example 17 Scrap to be Recovered: Cd—Zn—O Composite Oxide

As with Example 9, electrolysis was performed with pH 7 while periodically inverting the polarity to obtain hydroxide. The production yield was 98.1%.

As with Example 9, with the Cd—Zn—O composite oxide having conductive property, it was possible to efficiently recover a valuable resource (metal) as hydroxide.

Example 18 Scrap to be Recovered: Ga—Cu—O Composite Oxide

As with Example 9, electrolysis was performed with pH 10 while periodically inverting the polarity to obtain hydroxide. The production yield was 99.6%.

As with Example 9, with the Ga—Cu—O composite oxide having conductive property, it was possible to efficiently recover a valuable resource (metal) as hydroxide.

Example 19 Scrap to be Recovered: Sb—In—O Composite Oxide

As with Example 9, electrolysis was performed with pH 8 while periodically inverting the polarity to obtain hydroxide. The production yield was 98.7%.

As with Example 9, with the Sb—In—O composite oxide having conductive property, it was possible to efficiently recover a valuable resource (metal) as hydroxide.

Example 20 Scrap to be Recovered: Fe—Ge—O Composite Oxide

As with Example 9, electrolysis was performed with pH 7 while periodically inverting the polarity to obtain hydroxide. The production yield was 96.7%.

As with Example 9, with the Fe—Ge—O composite oxide having conductive property, it was possible to efficiently recover a valuable resource (metal) as hydroxide.

Example 21 Scrap to be Recovered: Pd—Sn—O Composite Oxide

As with Example 9, electrolysis was performed with pH 8 while periodically inverting the polarity to obtain hydroxide. The production yield was 97.8%.

As with Example 9, with the Pd—Sn—O composite oxide having conductive property, it was possible to efficiently recover a valuable resource (metal) as hydroxide.

Example 22 Scrap to be Recovered: Ti—In—O Composite Oxide

As with Example 9, electrolysis was performed with pH 7 while periodically inverting the polarity to obtain hydroxide. The production yield was 93.7%.

As with Example 9, with the Ti—In—O composite oxide having conductive property, it was possible to efficiently recover a valuable resource (metal) as hydroxide.

As shown in Examples 9 to 22 described above, even when using scraps of conductive oxides other than ITO, valuable metal can be efficiently recovered from the scrap containing conductive oxide as hydroxide or a mixture of hydroxide and subhydroxide by changing the polarity.

INDUSTRIAL APPLICABILITY

The method provided by the present invention is superior, since recovering valuable metal from scrap containing conductive oxide, such scraps as a sputtering target scrap of indium-tin oxide (ITO) containing conductive oxide or a scrap as mill ends of conductive oxide that arise during the production of such a sputtering target is simply subject to electrolysis as the anode and cathode. It is very easy to efficiently recover valuable metal as hydroxide or a mixture of hydroxide and subhydroxide, or as metal oxide or a mixture of two or more types of metal oxides.

Moreover, the recovery of valuable metal from scrap containing conductive oxide according to the present invention enables to maintain the purity without change if the scrap containing conductive oxide to be subject to electrolysis is in itself scrap of a high purity material, and the scrap can be recovered as high purity hydroxide or a mixture of hydroxide and subhydroxide, or as metal oxide or a mixture of two or more types of metal oxides.

This is a significant advantage of the present invention. The present invention yields superior effects of saving complicated processes and the process of eliminating impurities mixed in during production as in the past, enabling to improve the production efficiency and recover high purity valuable metal. Thus, the present invention is highly useful as a method of recovering valuable metal from scrap containing conductive oxide. 

1. A method of recovering valuable metal from scrap containing conductive oxide including the steps of using an insoluble electrode as either an anode or a cathode, using a scrap containing conductive oxide as the counter cathode or anode, performing electrolysis while periodically inverting the polarity, and recovering the scrap as hydroxide.
 2. The method of recovering valuable metal from scrap containing conductive oxide according to claim 1, wherein oxide system scrap is conductive oxide and a substance that can be reduced to metal or suboxide with hydrogen. 